      Product Description產品描述
      Lead-freePVC transparent compound are granule compounds which are manufactured with mixing, plasticizing and pelletizing process. They regard advanced PVC resin as the basic raw material, and add special plasticizer, stabilizer and other accessory ingredients.
      環保型聚氯乙烯透明料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、特種穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
       
      Characteristics and Application 特點及用途
      The products have excellent transparent properties, mechanical and physical properties and good processability. They can meet RoHS Standard. They are mainly used for the wire and cables and other materials which have transparent property requirements.
      產品具有良好的透明性和機械物理性能,加工性能優異,符合RoHS環保標準。主要用于有透明要求的材料。
       
      Processing Indicator加工工藝
      Recommend to use single-screw extruders with L/D= 20-25.
      建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
      Model
      牌號
      Machine Barrel Temperature
      機筒溫度
      Molding Temperature
      機頭溫度
      W-70(C) / W-90(C) 140-165℃ 165-175℃
       

      Physical and Electrical Properties
      機械物理性能及電性能指標

      Item

      試驗項目

      Unit
      單位
      Technical Requirements
      技術要求
      W-70(CJ) W-70(CH) W-90(CJ) W-90(CH)
      Tensile Strength
      拉伸強度
      MPa ≥15.0 ≥12.5 ≥15.0 ≥12.5
      Elongation at Break
      斷裂伸長率
      % ≥150 ≥200 ≥150 ≥200
      20℃Volume Resistivity
      20℃時體積電阻率
      Ω.m ≥1×1011 ≥1×108 ≥1×1011 ≥1×108
      200 Thermal Stability
      200℃時熱穩定時間
      min ≥50 ≥50 ≥50 ≥50
      Brittle Temperature with Impact
      沖擊脆化溫度
      -20±5 -35±5 -20±5 -35±5
      Hardness
      硬度
      Shore A 85±5 75±5 85±5 75±5
      Thermal Aging
      熱老化試驗
      \ 100℃×168h 100℃×168h 100℃×240h 100℃×240h
      Tensile Strength Variation
      拉伸強度變化率
      % ±30 ±30 ±30 ±30
      Elongation Variation
      斷裂伸長率變化率
      % ±30 ±30 ±30 ±30