      您所在的位置:網站首頁 > > 產品中心 > 彈性體材料 > PVC彈性體環保型聚氯乙烯/丁腈復合物彈性體絕緣料 W-7082 W-9082 W-0582
      環保型聚氯乙烯/丁腈復合物彈性體絕緣料 W-7082 W-9082 W-0582
      Lead-free Elastomeric PVC / NBR Insulation Compound...
      型號:0

      參考價:¥

      說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
      Product Description產品描述
      Lead-free elastomeric PVC/NBR insulation compounds are granule compounds which are manufactured with mixing, plasticizing and pelletizing processes. They regard advanced PVC resin and nitrile-butadiene rubberas the basic raw material, and add special plasticizer, stabilizer, flame retardant and other accessory ingredients.
      環保型聚氯乙烯/丁腈復合物彈性體絕緣料是以優質聚氯乙烯樹脂和丁腈橡膠為基料,加入特種增塑劑、穩定劑、阻燃劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
       
      Characteristics and Application 特點及用途
      These products have good oil-resistant property, soft and flexible, and good processability. They can meet RoHS Standard. They are mainly used for the insulation of oil-resistant cables, elevator cables, oil-resistant soft wires of dust cleaner, heavy soft cables and crane cables.
      產品具有良好的耐油性、彈性和柔軟性,加工性能優異,符合RoHS環保標準。主要用于有耐油要求的電線電纜、電梯電纜、耐油吸塵器軟線、重型軟線、起重機電纜等絕緣材料。
       
      Processing Indicator加工工藝
      Recommend to use of single-screw extruders with L/D= 20-25.
      建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
      Model
      牌號
      Machine Barrel Temperature
      機筒溫度
      Molding Temperature
      機頭溫度
      W-7082 / W-9082 / W-0582 145-170℃ 165-175℃
       

      Physical and Electrical Properties
      機械物理性能及電性能指標

      Item

      試驗項目

      Unit
      單位
      Technical Requirements
      技術要求
      W-7082 W-9082 W-0582
      Density
      比重
      \ ≤1.40 ≤1.40 ≤1.40
      Tensile Strength
      拉伸強度
      MPa ≥12.5 ≥12.5 ≥12.5
      Elongation at Break
      斷裂伸長率
      % ≥180 ≥180 ≥180
      Thermal Aging
      熱老化試驗
      \ 80℃×168h 100℃×240h 135℃×168h
      Tensile Strength Variation
      拉伸強度變化率
      % ±40 ±40 ±40
      Elongation Variation
      斷裂伸長率變化率
      % ±40 ±40 ±40
      Dielectric Strength
      介電強度
      MV/m ≥20 ≥20 ≥20
      200℃Thermal Stability
      200℃時熱穩定時間
      min ≥80 ≥120 ≥120
      20℃Volume Resistivity
      20℃時體積電阻率
      Ω.m ≥1×1011 ≥1×1011 ≥1×1011
      Brittle Temperature with Impact
      沖擊脆化溫度
      -30 -30 -30
      Oil Resistance
      耐油性能(ASTM 902)
      Temperature of Test試驗溫度 70 100 100
      Time of Test
      試驗時間
      h 24 24 24
      Tensile Strength Variation
      拉伸強度變化率
      % ±40 ±40 ±40
      Elongation Variation
      斷裂伸長率變化率
      % ±40 ±40 ±40
      Hardness
      硬度
      Shore A ≤75 ≤75 ≤75