      環保型聚氯乙烯彈性體護套料 W-7026 W-9026 W-0526
      Lead-free Elastomeric PVC Jacketing Compound...
      型號:0

      參考價:¥

      說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
      Product description產品描述
      Lead-free elastomeric PVC jacketing compounds are granular compounds which are manufactured through mixing, plasticizing and pelletizing processes. They regard advanced PVC resin as the basic raw materials, and add plasticizer, stabilizer and other accessory ingredients.
      環保型聚氯乙烯彈性體護套料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
       
      Characteristics and Application 特點及用途
      Those products have excellent mechanical and physical properties, soft and flexible, as well as good processability. They can meet RoHS Standard. They are mainly used for the jacketing of oil-resistant cables, elevator cables, oil-resistant soft wires of t dust collector, heavy soft wires, jacketing of crane cables and so on.
      產品具有良好的機械物理性能、彈性和柔軟性,加工性能優異,符合RoHS環保標準。主要用于有耐油要求的電線電纜、電梯電纜、耐油吸塵器軟線、重型軟線、起重機電纜等護層材料。
       
      Processing Indicator加工工藝
      Recommend to use single-screw extruders with L/D= 20-25.
      建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
      Model
      牌號
      Machine Barrel Temperature
      機筒溫度
      Molding Temperature
      機頭溫度
      W-7026 / W-9026 / W-0526 165-170℃ 175-185℃
       

      Physical and Electrical Properties
      機械物理性能及電性能指標

      Item

      試驗項目

      Unit
      單位
      Technical Requirements
      技術要求
      W-7026 W-9026 W-0526
      Density
      比重
      \ ≤1.40 ≤1.40 ≤1.40
      Tensile Strength
      拉伸強度
      MPa ≥12.5 ≥12.5 ≥12.5
      Elongation at Break
      斷裂伸長率
      % ≥250 ≥250 ≥250
      200℃Thermal Stability
      200℃時熱穩定時間
      min ≥80 ≥80 ≥80
      20℃Volume Resistivity
      20℃時體積電阻率
      Ω.m ≥1×108 ≥1×108 ≥1×108
      Dielectric Strength
      介電強度
      MV/m ≥18 ≥18 ≥18
      Brittle Temperature with Impact
      沖擊脆化溫度
      -40 -40 -40
      Hardness
      硬度
      Shore A ≤70 ≤70 ≤75
      Thermal Aging
      熱老化試驗
      / 100℃×168h 100℃×240h 135℃×168h
      Tensile Strength Variation
      拉伸強度變化率
      % ±30 ±30 ±30
      Elongation Variation
      斷裂伸長率變化率
      % ±30 ±30 ±30
      Oil Resistance
      耐油性能(ASTM 902)
      Temperature of Test試驗溫度 70 70 70
      Time of Test
      試驗時間
      h 4 4 4
      Tensile Strength Variation
      拉伸強度變化率
      % ±30 ±30 ±30
      Elongation Variation
      斷裂伸長率變化率
      % ±30 ±30 ±30