      Product Description 產品描述
      105℃lead-free automotive wire compound is granular compound which is manufactured through mixing, plasticizing and pelletizing processes. It regards advanced PVC resin as the basic raw materials, and adds plasticizer, stabilizer and other accessory ingredients. This product has excellent mechanical and physical properties, electrical property and good processability. It can meet RoHS Standard. The cables with it can meet LV112, VW60306, DIN72551 and other related standards. The highest working temperature is 105℃.
      環保型105℃汽車原線料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。產品具有良好的機械物理性能和電性能,加工性能優異,符合RoHS環保標準。制成電線后可以滿足LV 112、VW 60306、DIN 72551等相關標準,最高工作溫度為105℃。
       
      Product Details  產品明細
      Model
      牌號
      Application
      用途
      W-0596 >16mm2cables
      16mm2以上規格的電線
      W-0597 0.5mm2 ~6mm2 cables
      0.5mm2 ~6mm2及以規格的電線
      W-0598 ≤ 0.5mm2 cables
      0.5mm2及以下規格的電線
       
       
      Processing Indicator 加工工藝
      Recommend to use of single-screw extruders with L/D= 20-25.
      建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
      Model
      牌號
      Machine Barrel Temperature
      機筒溫度
      Molding Temperature
      機頭溫度
      W-0596 / W-0597 165-185℃ 180-190℃
      W-0598 165-185℃ 185-190℃
       
       
      Physical and Electrical Properties 機械物理性能及電性能指標

      Item

      試驗項目

      Unit
      單位
      Molding Temperature
      技術要求
      W-0596 W-0597 W-0598
      Density
      比重
      \ 1.32±0.02 1.32±0.02 1.32±0.02
      Tensile Strength
      拉伸強度
      MPa ≥18.0 ≥18.0 ≥18.0
      Elongation at Break
      斷裂伸長率
      % ≥250 ≥250 ≥250
      200℃Thermal Stability
      200℃時熱穩定時間
      min ≥200 ≥200 ≥200
      20℃Volume Resistivity
      20℃時體積電阻率
      Ω.m ≥1×1011 ≥1×1011 ≥1×1011
      Dielectric Strength
      介電強度
      MV/m ≥22 ≥20 ≥20
      Brittle Temperature with Impact
      沖擊脆化溫度
      -25 -25 -25
      Hardness
      硬度
      Shore A 88±2 94±2 97±2
      Thermal Aging
      熱老化試驗
      \ 136℃×168h
      Tensile Strength Variation
      拉伸強度變化率
      % ±20 ±20 ±20
      Elongation Variation
      斷裂伸長率變化率
      % ±20 ±20 ±20